LONGLITE® PBT 6030-200X
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oDQYK0_LONGLITE-PBT-6030-200X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT/PC 6030-200X is 30% glass fiber reinforced natural color injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.40 to 0.80 | % | |
| Flow | 0.10 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.4 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 24 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MBF 6010 H | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| KumhoSunny ABS HGX4400 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Innothane® IE-7000 | Innovative Polymers, Inc. | TSU | Innothane® |
| LNP™ VERTON™ RV00CESS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| Sumikon® PM-9750 | SBHPP | Phenolic | Sumikon® |