Vyncolit® X655/1
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oC33ML_Vyncolit-X655-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® X655/1 is a glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.08 | g/cm³ | ISO 1183 |
| Apparent Density | 1.04 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.16 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Post Shrinkage | 0.050 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.70 | % | ISO 178 |
| Tensile Modulus | 28000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.40 | % | ISO 527-2 |
| Flexural Modulus | 24000 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Compressive Stress | 360 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.7 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 211 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Transverse | 2.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 GB 30 | RTP Company | Nylon 66 | RTP |
| AT 280 | Celanese EVA Performance Polymers | LDPE | AT |
| Daelim Po1y® LH820 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Forprene® 6NM001A75 | SO.F.TER. SPA | TPV | Forprene® |
| HiFill FR® PC 1003 FR-NR UV | Techmer Engineered Solutions | PC | HiFill FR® |