Prime Impax 450 with VANISH
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Primex Plastics Corporation |
| Trademark: | Prime Impax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oBozyo_Prime-Impax-450-with-VANISH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Primex Corporation, along with our subsidiaries, are committed to sustainable practices that are ethical, responsible, and create value for customers, employees, and future generations. Complies with FDA Regulation 21 CFR 177.1640 Complies with UL 94HB at thickness' >.040" |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 83.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (> 1.02 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIBUR Synthetic Rubber SBR-1712 HI-AR Grade A | SIBUR, LLC | SBR, Unspecified | SIBUR Synthetic Rubber |
| Toyolac® 530-X01 | Toray Resin Company | ABS | Toyolac® |
| DAI-EL™ T-530 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| HiFill® POM HO GB20 LE | Techmer Engineered Solutions | Acetal (POM) Homopolymer | HiFill® |
| Plasmer 2065B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |