Latene® EP 22UVH2 MX/25
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oBHH17_Latene-EP-22UVH2-MX-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polypropylene copolymer (PPc). UV and thermally stabilised. Special mineral filler. Very good surface appearance. Good toughness properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 to 1.6 | % | |
| Flow | 1.3 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Continuous Use Temperature | 110 | °C | |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 400 | V | IEC 60112 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mold Shrinkage Pressure | 60.0 | MPa | ISO 294-4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP564 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| Ultramid® Endure D3G10 BK20560 | BASF Corporation | Nylon 66 | Ultramid® |
| Celstran® PA66-GF50-0112P7,5/10 | Celanese Corporation | Nylon 66/6 | Celstran® |
| Daelim Po1y® PR-770B | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| FLEXITEQ™ V70A010UV | Marplex Australia Pty. Ltd. | TPO (POE) | FLEXITEQ™ |