Order Products : sales@su-jiao.com
MAJORIS FC189C - 9444F
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oAxlNY_MAJORIS-FC189C---9444F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FC189C - 9444F is a mineral filled high performance compound intended for injection moulding. FC189C - 9444F is intended for component, which require very good surface quality, rigidity, low shrinkage and high dimensional stability. The product is UV stabilised, with anti fungi additive and fresh-clean fragrance. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2180 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 18 | % | ISO 527-2 |
| Flexural Modulus 1 | 1930 | MPa | ISO 178 |
| Flexural Stress | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 44 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilene F8235 | API Polymers, Inc. | PP Copolymer | Michilene |
| Sinvicomp SGH9505 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Nanjing Hongrui PBT T1303 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| DURACON® SW-22 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |
| K-vinyl 70 Deg C Rating Insulation (90-Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |