Rilsan® HT CMFO
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oAiO3w_Rilsan-HT-CMFO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® HT CMFO is a polyphthalamide produced from a renewable source. This grade, designed for injection, is the less viscous one in the Rilsan® HT family. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 45.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1750 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 58.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 190 | % | |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 260 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | > 65 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 270 to 310 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN 55180 | Saudi Polymers Company | HDPE | Marlex® |
| Spartech Polycom SC7-7022F | Spartech Polycom | PC | Spartech |
| TULAMID® PA-SV25 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Yanshan PE LD100 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Globalene® 6331F | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |