| PBT, non-reinforced, injection molding, flame retardant |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.47 | g/cm³ | ISO 1183 |
| Apparent Density | 0.90 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 250°C, 2.00mm 1 | 2.2 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.20 | % | ISO 2577 |
| Flow direction : 250°C, 2.00mm 3 | 2.2 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.20 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 150 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2760 | MPa | ASTM D638 |
| 23°C | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield, 23°C | 50.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 48.3 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 3.0 | % | ISO 527-2/50 |
| Fracture, 23°C | 16 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 8.0 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2800 | MPa | ISO 899-1 |
| 1000 hr | 1800 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| 23°C | 2560 | MPa | ASTM D790 |
| 23°C 5 | 3000 | MPa | ISO 178/A |
| Flexural Strength | |||
| 23°C | 85.5 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 80.0 | MPa | ISO 178/A |
| 23°C 6 | 90.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength (23°C) 7 | 5.0 | % | ISO 178/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halving Interval | IEC 60216 | ||
| Electric Strength | 12.4 | °C | IEC 60216 |
| Tensile Impact Strength : 1.50 mm | 9.2 | °C | IEC 60216 |
| Tensile Strength : 1.50 mm | 11.7 | °C | IEC 60216 |
| Temperature index | IEC 60216 | ||
| Electric Strength, 20000 hr | 145 | °C | IEC 60216 |
| Tensile Impact Strength, 20000 hr : 1.50 mm | 135 | °C | IEC 60216 |
| Tensile Strength, 20000 hr : 1.50 mm | 140 | °C | IEC 60216 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GFMHR, 11-030 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 90 | kJ/m² | ISO 179/1eU |
| 23°C | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 65 | kJ/m² | ISO 180/1U |
| 23°C | 80 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy (23°C, Energy to Peak Force) | 40.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 48.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 190 | °C | ISO 306/B120 |
| Ball Pressure Test (190°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.25 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp (1.50 mm) | 130 | °C | UL 746 |
| RTI (1.50 mm) | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.40 | IEC 60250 | |
| 23°C, 1 MHz | 3.20 | IEC 60250 | |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index 9 | 32 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® EP 7060 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Ultrason® E 2010 MR SW 10111 | BASF Corporation | PESU | Ultrason® E |
| ALCOM® PC 740/4 UV WT1368-04LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| CompaDur® 121 GK 30 black (032) | DimeLika Plast GmbH | PBT | CompaDur® |
| EPLAMID 6 FX2 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |