LONGLITE® PBT 3030-200FR
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oAMxKG_LONGLITE-PBT-3030-200FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT 3030-200FR is a 30% glass fiber reinforced impact modified hydrolysis resistant natural color injection molding grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 to 1.1 | % | |
| Flow | 0.10 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9600 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propak® 7021 | PolyPacific Pty. Ltd. | PP Homopolymer | Propak® |
| YUPLENE® HX3800 | SK Global Chemical | PP Homopolymer | YUPLENE® |
| Evermore PUR UDA-10X | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| HiFill® PA6/6 GF14 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Karina BEIGE PVC COMPOUND 800-08/52-A-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |