AVP™ FLT25CP
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oA74sN_AVP-FLT25CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVP™ FLT25CP is a Polycarbonate + PET (PC+PET) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.18 mm) | 49.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 90 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 2210 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 116 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.52 mm, BK, WT, GY | V-0 | ||
| 3.00 mm, BK, WT, GY | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 254 to 268 | °C | |
| Middle Temperature | 254 to 268 | °C | |
| Front Temperature | 260 to 274 | °C | |
| Nozzle Temperature | 254 to 268 | °C | |
| Processing (Melt) Temp | 266 to 279 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa | |
| Screw Speed | 25 to 50 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3405 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| RTP 506 | RTP Company | SAN | RTP |
| MTEGRITY™ PP Homopolymer PP100 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| ULTEM™ HU2110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| NYCOA Polyamide GR30 V0 Black | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |