Order Products : sales@su-jiao.com
VITAMIDE® AR38NT6513
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o9hXCs_VITAMIDE-AR38NT6513.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AR38NT6513 is a Polyamide 66 (Nylon 66) product filled with 40% glass fiber. It is available in Europe. Primary characteristic: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2.00 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 200 | MPa | ISO 527-2 |
| -- | 200 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 10500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 290 | MPa | ISO 178 |
| Yield | 290 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 12.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | 75.0 | ASTM D256 | |
| Charpy Unnotched Impact Strength | 75 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 255 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 2.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 35 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 450 | V | IEC 60112 |
| -- | 450 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 23 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® N8860 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| THERMOLAST® K TC8FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Bergamid™ A700 BK VN4255 LS | PolyOne Corporation | Nylon 66 | Bergamid™ |
| DeWAL DW 404BNC | DeWAL Industries | UHMWPE | DeWAL |
| Echo® RPC30G BK | Ravago Manufacturing Americas, LLC | PP Homopolymer | Echo® |