Generic LCP
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o8pD1T_Generic-LCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic LCP This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.38 - 2.70 | g/cm³ | ASTM D792 |
| 23°C | 1.40 - 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.010 - 0.40 | % | ASTM D955 |
| 23°C | -0.020 - 0.82 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 10000 - 37900 | MPa | ASTM D638 |
| 23°C | 7000 - 24300 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 110 - 182 | MPa | ISO 527-2 |
| 23°C | 44.8 - 100 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 0.40 - 5.8 | % | ASTM D638 |
| Fracture, 23°C | 1.4 - 6.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 7580 - 19300 | MPa | ASTM D790 |
| 23°C | 6800 - 12500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 68.6 - 159 | MPa | ASTM D790 |
| 23°C | 84.0 - 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 95 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 3.7 - 270 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 20 - 86 | J/m | ASTM D256 |
| 23°C | 4.0 - 95 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 59 - 1200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 232 - 293 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 165 - 315 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 10 - 4.0E+14 | ohms·cm | ASTM D257 |
| Relative Permittivity (23°C) | 4.39 | IEC 60250 | |
| Dissipation Factor (23°C) | 1.0E-3 - 0.035 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 - 151 | °C | |
| Drying Time | 3.0 - 8.2 | hr | |
| Dew Point | -29.2 - -28.9 | °C | |
| Hopper Temperature | 25.0 - 32.1 | °C | |
| Rear Temperature | 271 - 347 | °C | |
| Middle Temperature | 278 - 355 | °C | |
| Front Temperature | 283 - 364 | °C | |
| Nozzle Temperature | 292 - 370 | °C | |
| Processing (Melt) Temp | 287 - 373 | °C | |
| Mold Temperature | 78.2 - 137 | °C | |
| Injection Pressure | 98.4 - 121 | MPa | |
| Holding Pressure | 97.6 - 100 | MPa | |
| Back Pressure | 0.175 - 1.56 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic LCPThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V964A | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Taitacell EPS 321S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Wellamid® GF43-66/6 XE-N | Wellman Engineering Resins | Nylon 66/6 | Wellamid® |
| Forprene® 6SD001A75 | SO.F.TER. SPA | TPV | Forprene® |
| Tritan™ LX100 | Eastman Chemical Company | Copolyester | Tritan™ |