Sarlink® TPV 5765B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o8QOYg_Sarlink-TPV-5765B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® X-5765B4 is a UV stable low hardness grade possessing exceptional tensile strength, superior compression set, chemical resistance and high temperature performance. It can be easily processed by extrusion, injection molding or blow molding for various applications such as glass run channels, waistbelts, weatherstrips, seals and other profiles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.968 | g/cm³ | ASTM D792 |
| -- | 0.970 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A, 5 seconds, extruded | 65 | ASTM D2240, ISO 868 | |
| Shore A, 5 seconds, injection molding | 68 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Transverse flow : 100% strain | 2.70 | MPa | ASTM D412, ISO 37 |
| Flow : 100% strain | 4.20 | MPa | ASTM D412, ISO 37 |
| Tensile Strength | |||
| Transverse flow : Fracture | 7.10 | MPa | ASTM D412 |
| Flow : Fracture | 6.30 | MPa | ASTM D412, ISO 37 |
| Fracture | 7.10 | MPa | ISO 37 |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 570 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 320 | % | ASTM D412, ISO 37 |
| Tear Strength - Across Flow | |||
| -- | 29.8 | kN/m | ASTM D624 |
| -- 1 | 29 | kN/m | ISO 34-1 |
| Compression Set | |||
| 23°C, 22 hr | 21 | % | ASTM D395 |
| 70°C, 22 hr | 30 | % | ASTM D395 |
| 125°C, 70 hr | 44 | % | ASTM D395 |
| -5°C, 22 hr | 21 | % | ISO 815 |
| 21°C, 22 hr | 30 | % | ISO 815 |
| 52°C, 70 hr | 44 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | 5.0 | % | ASTM D573 |
| 100% strain, 135°C, 1000 hr | -13 | % | ASTM D573 |
| 150°C, 168 hr | -4.0 | % | ASTM D573 |
| 100% strain, 150°C, 168 hr | -7.0 | % | ASTM D573 |
| 100% strain 57°C, 1000 hr | 5.0 | % | ISO 188 |
| 66°C, 168 hr | -13 | % | ISO 188 |
| 100% strain 66°C, 168 hr | -4.0 | % | ISO 188 |
| 135°C, 1000 hr | -7.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | |||
| 135°C, 1000 hr | -2.0 | % | ASTM D573 |
| 150°C, 168 hr | -5.0 | % | ASTM D573, ISO 188 |
| 57°C, 1000 hr | -2.0 | % | ISO 188 |
| Change in Durometer Hardness in Air | |||
| Support a, 135°C, 1000 hr | 2.0 | ASTM D573 | |
| Support a, 150°C, 168 hr | 1.0 | ASTM D573, ISO 188 | |
| Support A, 57°C, 1000 hr | 2.0 | ISO 188 | |
| Change in Volume | |||
| 125°C, 70 hr, in IRM 903 oil | 91 | % | ASTM D471 |
| 125°C, 70 hr, in IRM 903 oil | 91 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Black) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary @ 206/s | |||
| 200°C | 340 | Pa·s | ISO 11443 |
| 200°C | 340 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 177 - 216 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 182 - 221 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Back Pressure | 0.0689 - 1.03 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 204 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 188 - 210 | °C | |
| Cylinder Zone 4 Temp. | 188 - 210 | °C | |
| Melt Temperature | 193 - 216 | °C | |
| Die Temperature | 193 - 216 | °C | |
| Take-Off Roll | 21.1 - 48.9 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 MeshScrew: General PurposeCompression Ratio: 3:1 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V221-86 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| alphalon™ E 40 LN | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Celanex® 3300FC | Celanese Corporation | PBT | Celanex® |
| Fainplast PVC RE 224 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Generic PP Alloy - Mineral | Generic | PP Alloy | Generic |