CONTINUUM™ DGDD-2480 NT
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o6llUn_CONTINUUM-DGDD-2480-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONTINUUM™ DGDD-2480 NT Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long term hydrostatic strength combined with outstanding resistance to slow crack growth and rapid crack propagation are desired. Suitable applications include natural gas distribution pipes, industrial piping, mining, sewage, and municipal water service lines. Industrial Standards Compliance
NOTES: (1) Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 (6.5%). |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D1505 | ||
| Natural | 0.949 | g/cm³ | |
| Black 1 | 0.959 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 8.5 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | > 24.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790B |
| Resistance to Rapid Crack Propagation, Pc 4 | > 46.0 | bar | ISO 13477 |
| Resistance to Rapid Crack Propagation, Tc 5 | < -17 | °C | ISO 13477 |
| Slow Crack Growth PENT - @ 2.4 MPa 6(80°C) | > 5000 | hr | ASTM F1473 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability | > 220 | °C | ASTM D3350 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 7(23°C) | 490 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 8 | < -75.0 | °C | ASTM D746A |
| Note Message | |
|---|---|
| 1 . | Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 (6.5%). |
| 2 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 3 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 4 . | Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 5 . | Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 6 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 7 . | Compression molded parts prepared according to ASTM D 4703, Procedure C. Properties will vary with changes in molding conditions and aging time. |
| 8 . | Compression molded parts prepared according to ASTM D 4703, Procedure C. Properties will vary with changes in molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 283 TFE 10 HS | RTP Company | Nylon 66 | RTP |
| Sindustris PBT GP2307FY | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Tarnamid® T-27 GF 15 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| TOLEN H007 EX | SIBUR, LLC | PP Homopolymer | TOLEN |
| ADDINYL B2I V25 | ADDIPLAST | Nylon 6 | ADDINYL |