Moplen EP240H
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o6IW87_Moplen-EP240H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EP240H is a nucleated heterophasic copolymer, suitable for injection moulding as well as for thermoforming applications. It exhibits excellent low temperature impact behavior combined with a good processability. Moplen EP240H is typically used for crates in addition to thermoformed margarine tubs. Moplen EP240H is suitable for food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 2.70 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 44.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 8.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 8.0 | kJ/m² | |
| 0°C | 12 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ||
| 0°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -47.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A50 |
| -- | 60.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 73 | DIN 67530 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-7753 | Quantum Composites Inc. | Polyester, TS | Quantum Composites |
| Shinkolite PX | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | Shinkolite |
| Niretan B C35 | Soredi S.p.a. | Nylon 6 | Niretan B |
| Hyundai EP Adhesives RE140R/1002 | HYUNDAI EP Co., Ltd. | PP, Unspecified | Hyundai EP Adhesives |
| LNP™ LUBRICOMP™ RAL229 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |