Tenopom® POM B3 G30 PRTA011 PR309
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Tenopom® POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o61any_Tenopom-POM-B3-G30-PRTA011-PR309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyacetal copolymer in black color with 30% glass fiber, easy processing. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 to 1.60 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.0 to 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 7800 | MPa | ASTM D790 |
| Flexural Strength | 150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 144 | °C | ASTM D648 |
| Peak Melting Temperature | 164 to 167 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TROGAMID® TCR Film 400 µm | Evonik Industries AG | Nylon, Unspecified | TROGAMID® TCR Film |
| XYRON™ L524V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| ULTRATUF™ SG | Spartech Plastics | PC | ULTRATUF™ |
| Bergamid™ B700 UF black | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Evoprene™ G 992 | AlphaGary | SEBS | Evoprene™ G |