Asaflex™ 840
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | AKelastomers |
| Trademark: | Asaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o43tcf_Asaflex-840.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection molding, inflation molding, and sheet extrusion grade. Blended with GPPS (general-purpose polystyrene) or SC*, for products with well-balanced performance characteristics and good thermal characteristics. It is supplied in pellet form. In blends with GPPS, for PSP* laminate films. In blends with SC, for shrink films and other products. * Styrenic copolymer from PS Japan Corp. similar to Asaflex™ 840 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS . |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 10 | ISO 2039-2 | |
| Shore Hardness (Shore D) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 40 | % | ISO 527-2/5 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Flexural Stress | 34.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Complete Break) | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 62.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 81.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 88.0 | % | ISO 3537 |
| Haze (2000 µm) | 1.2 | % | ISO 3537 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4405 TFE 5 | RTP Company | Nylon, Unspecified | RTP |
| TRIREX® Compound 3000H | Samyang Corporation | PC | TRIREX® Compound |
| Expandable PS RP33W | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Eastar™ GN078 | Eastman Chemical Company | Copolyester | Eastar™ |
| Elastollan® C 78 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |