Reny® 1021UCS
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o3edLa_Reny-1021UCS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® 1021UCS is a Polyarylamide (PARA) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1021UCS: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.61 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 13 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 11.1 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.47 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17800 | 14400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 252 | 184 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.4 | % | ISO 527-2 |
| Flexural Modulus | 18300 | 13800 | MPa | ISO 178 |
| Flexural Stress | 392 | 305 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 87 | 100 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 227 | 221 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 217 | 210 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 145 | Salflex Polymers Ltd. | TPO (POE) | Salflex |
| Xuchuan 6170/B-8280 (Mid-sole) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| EL-Pro™ P700J | SCG Chemicals Co., Ltd. | PP Homopolymer | EL-Pro™ |
| ENVIRON® ENV39-NC410 | ENVIROPLAS®, Inc. | PC+PBT | ENVIRON® |
| Huafon HF-3190A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |