Leona™ 13G43
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | o3UION_Leona-13G43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ 13G43 is a Polyamide 66 (Nylon 66) product filled with 43% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 13G43 include automotive, electrical/electronic applications and engineering/industrial parts. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.50 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 1.4 | % | |
| Equilibrium, 23°C, 50% RH | -- | 1.4 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785, ISO 2039-2 | |||
| M-Scale | 96 | 80 | ||
| R-Scale | 118 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12700 | 10200 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 207 | 150 | MPa | ISO 527-2 |
| -- | 196 | 157 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 3.0 | 4.0 | % | ASTM D638 |
| Break, 23°C | 3.0 | 4.5 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 11800 | 8300 | MPa | ASTM D790 |
| 23°C | 11700 | 8700 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 314 | 235 | MPa | ASTM D790 |
| 23°C | 303 | 225 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | -- | 19.0 | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 12 | 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 84 | 85 | kJ/m² | ISO 179 |
| Notched Izod Impact | 130 | 210 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.40 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ GT3 300 H G40 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ GT3 |
| YUZEX® 7303S | SK Global Chemical | HDPE | YUZEX® |
| Nipol® 1561 | Zeon Corporation | Latex | Nipol® |
| Elastron® G G601.A45.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Pearlthane® 11T92EM | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |