| PA 66, non-reinforced, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 280°C, 2.00 mm 1 | 1.2 | -- | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.11 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 1.1 | -- | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.42 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 151 | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3500 | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress | ||||
| Yield, 23°C | 94.0 | 55.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 80.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ||||
| Yield, 23°C | 4.2 | 20 | % | ISO 527-2/50 |
| Break, 23°C | 11 | 230 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 10 | 160 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 3200 | 1300 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% Strain | 105 | 36.0 | MPa | ISO 178/A |
| 23°C | 127 | 49.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 6.2 | 8.0 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GFHR, 14-030; ISO 1043-PA FR (30) | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | < 5.0 | min | |
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 9 | 5.10 | -- | J | |
| -- 10 | 13.1 | 27.2 | J | |
| Film Puncture Force | ISO 6603-2 | |||
| -- 11 | 2400 | -- | N | |
| -- 12 | 3730 | 4630 | N |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 120 | 190 | kJ/m² | |
| 23°C | 110 kJ/m² | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 110 | 130 | kJ/m² | |
| 23°C | 80 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | > 230 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (249°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 13 | 265 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | -- | V | |
| Solution B 14 | 400 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 775 | -- | °C | |
| 1.50 mm | 775 | -- | °C | |
| 3.00 mm | 775 | -- | °C | |
| Oxygen Index 15 | 30 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | US-FMVSS302 |
| 9 . | -30°C |
| 10 . | 23°C |
| 11 . | -30°C |
| 12 . | 23°C |
| 13 . | 10°C/min |
| 14 . | Depth of Erosion: 1.80 mm |
| 15 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 221 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Sylvin 9077-88 Grey 9434 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nylene® 132L | Custom Resins Group | Nylon 66 | Nylene® |
| LNP™ LUBRICOMP™ JCL36E compound | SABIC Innovative Plastics | PESU | LNP™ LUBRICOMP™ |
| ULTEM™ SF2350 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |