SABIC® PP 505P
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nzIF3s_SABIC-PP-505P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 505P is a multi purpose grade for extrusion and injection moulding applications. SABIC® PP 505P provides an excellent stretch ability and is suitable for extrusion of tapes, strapping, high tenacity yarns but also for thermoformed articles. For injection moulded parts SABIC® PP 505P shows a moderate stiffness, good impact resistance and very good surface hardness. SABIC PP505P is suitable for production of caps and closures and house ware articles. SABIC® PP 505P is a low mfi grade typically used in extrusion applications like sheet and thermoforming. SABIC® PP 505P is typically used in dairy, flower pots, yellow fats and disposables plates and cups. However, customers use this grade also in combination with fillers like Talc and CaCO3. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1500 | MPa | ASTM D638 |
| -- | 1500 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 36.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 10 | % | ASTM D638 |
| Yield | 10 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256A |
| 23°C | 3.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525, ISO 306/A 6 6 |
| -- | 88.0 | °C | ASTM D1525, ISO 306/B 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2201H0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| tefabloc® TP SD 333 60A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Akulon® K224-G7 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Generic PP Alloy | Generic | PP Alloy | Generic |
| Kotex K-30UVR | Kotec Corporation | PC | Kotex |