ISPLEN® PB 154 M1F
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nyqgLp_ISPLEN-PB-154-M1F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEW ISPLEN® PB154M1F is a medium melt flow rate heterophasic polypropylene, especially developped for films with a high impact strenght even at low temperatures. Its special structural characteristics provide it high impact strength, good processability, high tear strength and better optical properties than convencional heterophasic copolymers. Additionally, this grade includes both antiblock and slip agents. APPLICATIONS. Non oriented film extrusion where high impact and tear strength are essential:
Its recommended melt temperature range goes from 190 to 250°C. Processing conditions may be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Injection Molded) | 1100 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress - MD | ISO 527-3 | ||
| Yield, 50 µm | 17.0 | MPa | |
| Break, 50 µm | 34.0 | MPa | |
| Elmendorf Tear Strength (50 µm) | 0.95 | N | ISO 6383-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 15 | kJ/m² | ISO 179 |
| Multi-Axial Instrumented Impact Energy (-20°C, 1.00 mm, Injection Molded) | 9.50 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (-20°C, 1.00 mm, Injection Molded) | 1790 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 82.0 | °C | ISO 75-2/B |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm) | 43 | ASTM D2457 | |
| Haze (50.0 µm) | 22 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® MRGF25/15 42H-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| ARCEL® 640 (3.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| ELASTOSIL® LR 3003/10 TR A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Elastron® G G101.A83.N | Elastron USA, Inc. | SEBS | Elastron® G |
| LAMINEX® 2100 | Schwartz Technical Plastic | PF | LAMINEX® |