Sumikon® RX-6552S
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nyqGUQ_SumikonRX6552S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® RX-6552S Type Green is a Short Glass fiber & Mineral molding compound based on Phenolic Novolac polymer. It is supplied in the form of Granular/Molding Powder for Molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.24 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.060 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 121 | MPa | JIS K6911 |
| Flexural Modulus | 18100 | MPa | JIS K6911 |
| Flexural Strength | 246 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.6 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 241 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | JIS K6911 | ||
| -- 1 | 1.0E+12 | ohms | JIS K6911 |
| -- 2 | 3.0E+11 | ohms | JIS K6911 |
| Note Message | |
|---|---|
| 1 . | As molded |
| 2 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polypropylene DGF080.00 ESU | Trinseo | TPO | Polypropylene |
| Starex GR-4020 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| EMPILON® 8894 | EMPILON | SEBS | EMPILON® |
| Alpha PVC 2222C-85 | Mexichem Specialty Compounds Inc. | PVC, Unspecified | Alpha PVC |
| LEXAN™ LUX9610 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |