Baytec® MS-052 (BDO)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nxEGLP_Baytec-MS-052-BDO-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec MS-052 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer used in the manufacture of high-property solid cast polyurethane elastomers. When extended with 1,4-butanediol, this material complies with FDA regulation 21 CFR 177.2600 (Rubber Articles Intended for Repeated Use) and may be used for wet and dry repeated-use food-contact applications. When extended with HQEE, it complies with 21 CFR 177.1680 (Polyurethane Resins) and may be used for repeated-use food contact only with dry foods having no free surface fats or oils. As with any product, use of Baytec MS-052 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 16.0 | mg | ASTM D4066 |
| Compression Deflection | ASTM D575 | ||
| 10% | 1.46 | MPa | ASTM D575 |
| 15% | 2.28 | MPa | ASTM D575 |
| 2% | 0.0552 | MPa | ASTM D575 |
| 20% | 3.07 | MPa | ASTM D575 |
| 25% | 3.93 | MPa | ASTM D575 |
| 5% | 0.600 | MPa | ASTM D575 |
| 50% | 11.9 | MPa | ASTM D575 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 4.69 | MPa | ASTM D412 |
| 200% strain | 6.76 | MPa | ASTM D412 |
| 300% strain | 10.2 | MPa | ASTM D412 |
| Tensile Strength (Break) | 37.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 530 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 91.1 | kN/m | ASTM D624 |
| Cracking | 26 | kN/m | ASTM D1938 |
| Compression Set (70°C, 22 hr) | 24 | % | ASTM D395 |
| Bayshore Resilience | 52 | % | ASTM D2632 |
| Additional Information |
|---|
| Appearance: Straw yellow liquidNCO: 5.10 to 5.50 wt%Flash Point, PMCC: >93°CSpecific Gravity at 80°C: 1.12Specific Gravity at 100°C: 1.11Viscosity at 80°C: 3270 mPa-sViscosity at 100°C: 1660 mPa-sNCO/OH Ratio: 1.05Stoichiometry: 95% TheoryPrepolymer Temperature: 80 to 90°CExtender Temperature: 50 to 70°CMold Temperature: 90 to 100°CPot Life: 5 to 9 minDemold: 30 to 40 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResinDirect HIPS8UL | ResinDirect | PS (HIPS) | ResinDirect |
| WPP PP PPC3GF2-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| AIE PET 40G6F | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| Hanwha Total PP RB210 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina YELLOW PVC COMPOUND 350-02/249 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |