PRL ABS-FR-UV-(f2)
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nwBuzC_PRL-ABS-FR-UV--f2-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL ABS-FR-UV-(f2) is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in North America. Typical application: Outdoor Applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.0 to 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Outdoor Suitability (All Colors) | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 2280 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 40.7 | MPa | |
| Break, 3.18 mm | 37.9 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 2.2 | % | |
| Break, 3.18 mm | 10 | % | |
| Flexural Modulus (3.18 mm) | 2380 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 210 | J/m | ASTM D256 |
| -30°C | 6.3 | kJ/m² | ISO 180/1A |
| 23°C | 19 | kJ/m² | ISO 180/1A |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 87.8 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 82.2 | °C | |
| Vicat Softening Temperature | 90.6 | °C | ASTM D1525 1 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-0 | ||
| 3.00 mm, ALL | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 171 to 182 | °C | |
| Middle Temperature | 199 to 210 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 204 to 232 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 U0 | NUREL, S.A. | Nylon 6 | Promyde® |
| TEKNIFLEX® VPA7400 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| Escorene™ Ultra FL 00206 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Kepital® FA-20 | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| HOPELEN SY-130 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |