LNP™ STAT-LOY™ A3000T compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nw7nI8_LNP-STAT-LOY-A3000T-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY A3000T is a compound based on ABS. Added features of this grade include: Antistatic, Clear. Also known as: LNP* STAT-LOY* Compound A- CLEAR Product reorder name: A3000T |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.83 | % | ISO 294-4 |
| Flow : 24 hr | 0.68 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.80 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1220 | MPa | ASTM D638 |
| -- | 1140 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 32.0 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2/5 |
| Break 3 | 24.0 | MPa | ASTM D638 |
| Break | 24.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 39 | % | ASTM D638 |
| Break | 63 | % | ISO 527-2, ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 1480 | MPa | ASTM D790 |
| -- 6 | 1420 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 42.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 42.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 8 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 81.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 81.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 68.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 9.0 to 11 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene Lumicene® M 2735 | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| BP Flex D 5512 RU BLK | Buckeye Polymers, Inc. | TPO | BP Flex |
| Hanwha Total PP RP100 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hipolyene 5198 FLM | Zylog Plastalloys | TPO (POE) | Hipolyene |
| PENTAMID B GV10 GK20 H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |