CELEX™ 310HF.B
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CELEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nuXDwq_CELEX-310HF-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CELEX™ 310HF.B glass fiber reinforced polycarbonate Resin is a 10% glass fiber reinforced polycarbonate material. It provides a property balance of easy flow, superior ignition resistance, high rigidity, dimension stability and heat resistance. It provides the injection molded part with good aesthetics. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 4050 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5140F1 | Spartech Polycom | PP, Unspecified | Spartech |
| Ferro PP MPP40FJ15NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| ELASTOSIL® N 288 | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| LG ABS ER461 | LG Chem Ltd. | ABS | LG ABS |
| LNP™ LUBRICOMP™ DFL22ER compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |