PETLIN LD N103X
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PETLIN (MALAYSIA) SDN BHD |
| Trademark: | PETLIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ntXqRe_PETLIN-LD-N103X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETLIN LD N103X is a low density polyethylene resin for heavy duty film applications. It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free) additives. It is intended primarily for blown film process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.70 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 45 | µm | |
| Film Thickness - Recommended / Available | 45 to 280 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| MD : 45 µm | 245 | MPa | |
| TD : 45 µm | 260 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 45 µm | 30.0 | MPa | |
| TD : Break, 45 µm | 27.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 45 µm | 170 | % | |
| TD : Break, 45 µm | 550 | % | |
| Dart Drop Impact (45 µm) | 270 | g | ASTM D1709 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 45 µm | 20000 | N | |
| TD : 45 µm | 25000 | N |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 45.0 µm) | 43 | ASTM D2457 | |
| Haze (45.0 µm) | 14 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE LD2920B | Trademark Plastics Corporation | LDPE | Trademark PE |
| Wondel® B BN0 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| NILENE® E10 K25T | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| ExxonMobil™ PP1013H1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Osterlene® PPC-80-1.2-N | Osterman & Company | PP Impact Copolymer | Osterlene® |