NOVA PC 1023R
| Category: | PC , Polycarbonate |
| Manufacturer: | NOVA Polymers, Inc. |
| Trademark: | NOVA PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nsqRwQ_NOVA-PC-1023R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVA PC 1023R is a polycarbonate (PC) material,. This product is available in North America and is processed by injection molding. The main features of NOVA PC 1023R are:
|
| General Information | |
|---|---|
| Additive |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.18 mm) | 62.1 | MPa | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2210 | MPa | ASTM D790 |
| Flexural Strength (Yield, 3.18 mm) | 94.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.18 mm | V-2 | UL 94 | |
| 6.35 mm | V-2 | UL 94 |
| Additional Information |
|---|
| Moisture Content, ASTM D 4019-88: <0.04 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 MS 5 | RTP Company | Nylon 66 | RTP |
| Solef® 31508 | Solvay Specialty Polymers | PVDF | Solef® |
| Verolloy B5736 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| ESTACARB PC 0820 V0 | Cossa Polimeri S.r.l. | PC | ESTACARB |
| Iupilon® EGN2020R2 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |