| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Lucent Polymers, Inc. |
| Trademark: | Lucent PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nsn9iU_Lucent-PP-CPP-240.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
|
40% Calcium Carbonate Filled, Impact Modified Polypropylene Melt Flow Adjustable for Application Colors Available Add "U" for UV Stabilized Add "H" for Heat Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 38.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.6 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bapolene® PP5062 | Bamberger Polymers, Inc. | PP Copolymer | Bapolene® |
| DAI-EL™ G-9062 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Karina WHITE PVC COMPOUND -E 830-10/150-Y-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubriOne™ AT-000/18T 2S | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| Hifax CA 1110 G2 HF C11306 | LyondellBasell Industries | PP Copolymer | Hifax |