DOWLEX™ 2042E
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nsahGe_DOWLEX-2042E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™2042E polyethylene resin is an ethylene/1-octene copolymer, which is suitable for the production and processing of blown films. These blown films require good tear strength, excellent toughness, good stiffness and high temperature resistance. Remarks: When used in the application field of contact with food, DOWLEX 2042E polyethylene resin should comply with the U.S. Food and Drug Administration regulations when it is unmodified and the processing process follows the requirements of good manufacturing practices. The requirements of the 177.1520, the Canadian Health Products and Food Agency (HPFB) -no objection (with restrictions) and the requirements of the food contact regulations of most European countries. Please contact your nearest Dow representative for proof of compliance with the food contact law. The purchaser remains responsible for determining whether the use of its products complies with all relevant regulations. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 2% Secant (Compression Molded) | 340 | MPa | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy (25 µm) | 1.00 | J | Internal method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 14.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 17.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 42.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 41.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 830 | % | ASTM D882 |
| TD : Break, 25 µm | 1100 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 100 | g | ASTM D1922 |
| TD : 25 µm | 620 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 2 | 118 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 25.0 µm) | 30 | ASTM D2457 | |
| Haze (25.0 µm) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 管形薄膜挤出的制造条件： 熔体温度：190 至 240°C。 放大比范围：1.5 至 3:1 建议的厚度范围：10 至 150 µm。 |
| Note Message | |
|---|---|
| 1 . | Compression molding |
| 2 . | Compression molding |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADEKA Y65-55 | Adeka Corporation | PUR-Ester | ADEKA |
| Karina RED PVC COMPOUND 813D42/46-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom 5340 D T 2 S | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sumiliteresin® PR-9480 | SBHPP | Phenolic | Sumiliteresin® |
| ULTEM™ 2110EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |