Ultramid® 8233G HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nqsyMD_Ultramid-8233G-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8233G HS BK-102 is a heat stabilized, black pigmented,33% glass fiber reinforced PA6 injection molding compound. The higher glass fiber reinforcement results in excellent strength, stiffness, high temperature performance and dimensional stability with a high resistance to creep under load. The heat stabilizer system extends properties at elevated temperatures. It offers easy processing and good aesthetics. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. It is suited for metal replacement. Applications Ultramid 8233G HS BK-102 is generally recommended for applications such as chain saw, power tool housings, weed trimmer components, gears, automotive window hardware, under hood applications including cables, fittings, cooling fans, electrical connectors and coil bobbins. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.1 | -- | % | ISO 62 |
| Saturation | 6.4 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.4 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.8 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 10300 | -- | MPa | |
| 23°C | 10200 | 5600 | MPa | |
| 80°C | 4820 | -- | MPa | |
| 121°C | 4010 | -- | MPa | |
| Tensile Strength | ||||
| Break, -40°C | 230 | 215 | MPa | ASTM D638 |
| Break, 23°C | 180 | 99.0 | MPa | ASTM D638 |
| Break, 80°C | 90.0 | 70.0 | MPa | ASTM D638 |
| Break, 121°C | 70.0 | 60.0 | MPa | ASTM D638 |
| Break, -40°C | 230 | -- | MPa | ISO 527-2 |
| Break, 23°C | 170 | 99.0 | MPa | ISO 527-2 |
| Break, 80°C | 90.0 | -- | MPa | ISO 527-2 |
| Break, 121°C | 70.0 | -- | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, -40°C | 3.0 | 2.5 | % | ASTM D638 |
| Break, 23°C | 3.5 | 7.0 | % | ASTM D638 |
| Break, 80°C | 7.0 | 6.5 | % | ASTM D638 |
| Break, 121°C | 7.0 | 6.5 | % | ASTM D638 |
| Break, 23°C | 3.0 | 7.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 8990 | -- | MPa | ASTM D790 |
| 23°C | 8500 | 5200 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 280 | -- | MPa | ASTM D790 |
| 23°C | 245 | 130 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 65 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 110 | -- | J/m | ASTM D256 |
| Drop Impact Resistance (23°C) | 4.07 | -- | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 218 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 208 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 3.8E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.600 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Footwear GF-6107 | S&E Specialty Polymers, LLC | PVC+NBR | S&E Footwear |
| Sarlink® TPE ME-2275B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| Cevian®-V 770 | PlastxWorld Inc. | ABS | Cevian®-V |
| Sylvin 4299-50 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Grilamid® L XE 10987 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |