E-RIALFILL H 15 40 T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nnRCMq_E-RIALFILL-H-15-40-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PP homopolymer obtained by recycling industrial scraps, 40% mineral filled. High flowability for injection molding, good dimensional stability and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 1.1 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.030 | % | ISO 62 |
| Ash Content | 40 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 3.00 | MPa | |
| Break, 23°C | 10.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 25 | % | |
| Break, 23°C | 22 | % | |
| Flexural Modulus 2(23°C) | 3500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 2.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 128 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A50 |
| -- | 94.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RBW Reprocessed Extrusion Grade | RBW Technologies, Inc. | HDPE | RBW |
| Bayflex® 110-50 (15% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| CP PRYME® Polyethylene PE100LD-.7FM | Chase Plastics Services Inc. | LDPE | CP PRYME® Polyethylene |
| GLS Acetal UN02 | GLS Polymers Pvt. Ltd. | Acetal (POM) Copolymer | GLS Acetal |
| KOPLA PP KPZ1022 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |