LNP™ LUBRICOMP™ QCL349 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nmQG83_LNPLUBRICOMPQCL349compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QCL349 is a compound based on Nylon 6/10 resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Internally Lubricated, Flame Retardant, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound QCL-4034 FR-1 Product reorder name: QCL349 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.78 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.11 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16500 | MPa | ASTM D638 |
| -- | 15800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 169 | MPa | ASTM D638 |
| Yield | 162 | MPa | ISO 527-2 |
| Fracture | 159 | MPa | ASTM D638 |
| Fracture | 162 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.8 | % | ASTM D638 |
| Yield | 1.7 | % | ISO 527-2 |
| Fracture | 1.9 | % | ASTM D638 |
| Fracture | 1.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 13100 | MPa | ASTM D790 |
| -- | 13000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 241 | MPa | ASTM D790 |
| -- | 239 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.34 | ASTM D3702 Modified | |
| With Self-Static | 0.28 | ASTM D3702 Modified | |
| Wear Factor - Washer | 444 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 530 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.20 | J | ASTM D3763 |
| -- | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 218 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 218 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 200 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 198 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOFORCE® PEEK C2301 | LEIS Polytechnik - polymere Werkstoffe GmbH | PEEK | TRIBOFORCE® |
| Vandar® 2100UV | Celanese Corporation | PBT | Vandar® |
| Nypol® PA C3 T30 NTLA010 NS304 | Petropol Industry and Trade of Polymers LTDA | Nylon 66/6 | Nypol® PA |
| Sylvin 83014-95FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 29168-70 Grey 9605 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |