LEMALLOY® PX603Y
| Category: | PPE+PP , Polyphenylene Ether + PP |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | LEMALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nm1cFK_LEMALLOY-PX603Y.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEMALLOY® PX603Y is a Polyphenylene Ether + PP (PPE+PP) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of LEMALLOY® PX603Y: High Flow. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 55.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 1.1 to 1.3 | % | |
| Flow : 3.20 mm | 1.0 to 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 42.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 1900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 59.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 120 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 250 to 290 | °C | |
| Nozzle Temperature | 250 to 290 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TC-C-29 FR | RTP Company | Nylon 66 | RTP |
| Amodel® A-4122 NL WH 905 | Solvay Specialty Polymers | PPA | Amodel® |
| Dryflex® A1 600601 | ELASTO | SEBS | Dryflex® |
| Ecomass® 1002ZC85 | Ecomass Technologies | Nylon Copolymer | Ecomass® |
| INTEGRAL™ 625 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |