Generic PPS - Carbon Fiber
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nksHGF_Generic-PPS---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPS - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.36 - 1.57 | g/cm³ | ASTM D792 |
| 23°C | 1.40 - 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.040 - 0.20 | % | ASTM D955 |
| Transverse flow : 23°C | 0.29 - 0.92 | % | ASTM D955 |
| 23°C | 0.12 - 0.41 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.015 - 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 100 - 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 9620 - 35200 | MPa | ASTM D638 |
| 23°C | 11100 - 45000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 57.0 - 102 | MPa | ASTM D638 |
| Fracture, 23°C | 157 - 160 | MPa | ASTM D638 |
| Fracture, 23°C | 169 - 176 | MPa | ISO 527-2 |
| 23°C | 89.6 - 207 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 0.50 - 1.5 | % | ASTM D638 |
| Fracture, 23°C | 0.50 - 1.7 | % | ASTM D638 |
| Fracture, 23°C | 0.68 - 1.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8790 - 31500 | MPa | ASTM D790 |
| 23°C | 12900 - 24700 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 162 - 291 | MPa | ASTM D790 |
| 23°C | 150 - 284 | MPa | ISO 178 |
| Yield, 23°C | 110 - 296 | MPa | ASTM D790 |
| Coefficient of Friction | 0.14 - 0.47 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.2 - 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 15 - 25 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 42 - 55 | J/m | ASTM D256 |
| 23°C | 4.9 - 8.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 150 - 500 | J/m | ASTM D256 |
| 23°C | 15 - 31 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 275 - 280 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 259 - 272 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 259 - 270 | °C | ISO 75-2/A |
| CLTE - Flow | |||
| -- | 3.6E-6 - 2.1E-5 | cm/cm/°C | ASTM D696 |
| -- | 8.6E-6 - 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 - 2.5E+7 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0 - 1.4E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 119 - 151 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 295 - 326 | °C | |
| Middle Temperature | 304 - 330 | °C | |
| Front Temperature | 313 - 339 | °C | |
| Processing (Melt) Temp | 318 - 331 | °C | |
| Mold Temperature | 119 - 159 | °C | |
| Injection Pressure | 85.3 - 86.4 | MPa | |
| Back Pressure | 0.258 - 0.620 | MPa | |
| Screw Speed | 45 - 100 | rpm | |
| Clamp Tonnage | 1.4 - 9.0 | kN/cm² |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPS - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AL 200 Black | Radici Plastics | Nylon 66 | Radilon® |
| Geon™ Vinyl Dry Blend E7370 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |
| Lifoflex® UV FLAM 30600 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| LNP™ THERMOCOMP™ KB006 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |
| Sylvin 3299-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |