Order Products : sales@su-jiao.com
OxyShield® Plus 1500
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | OxyShield® Plus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | niikbt_OxyShield-Plus-1500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OxyShield® Plus 1500 is a 15 micron biaxially oriented nylon film having a very high barrier to oxygen and other gases. The film provides excellent mechanical properties at high and low temperatures and excellent toughness and puncture resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.20 | ASTM D1894 | |
| With self-dynamics | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 15 µm | 2550 | MPa | ASTM D882 |
| TD : 15 µm | 2100 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 15 µm | 272 | MPa | ASTM D882 |
| TD : Break, 15 µm | 310 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 120 | % | ASTM D882 |
| TD : Break, 15 µm | 90 | % | ASTM D882 |
| Oxygen Permeability | ASTM D3985 | ||
| 25°C, 15 µm, 0% RH | 1.2 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| 25°C, 15 µm, 65% RH | 1.5 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (15 µm, 38°C, 100% RH) | 350 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 15.0 µm) | 108 | ASTM D2457 | |
| Haze (15.0 µm) | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield: 40189 in²/lbTensile Strength @ Break, ASTM D 882, MD: 35000 to 44000 psiTensile Strength @ Break, ASTM D 882, TD: 40000 to 50000 psiElongation @ Break, ASTM 882, MD: 110 to 130%Elongation @ Break, ASTM 882, TD: 80 to 100%Secant Modulus, ASTM D 882, MD: 320000 to 420000 psiSecant Modulus, ASTM D 882, TD: 255000 to 355000 psiCoefficient of Friction, ASTM D 1894: 0.4 to 0.6 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.1 to 0.3 vs Metal-DynamicDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 1.0 to 2.0% shrinkageCorona Treatment, ASTM D5946, treated side: 54 to 56 dynes/cmCorona Treatment, ASTM D5946,untreated side: 48 to 50 dynes/cm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CompaDur® 121 GF 30 FR black (040) | DimeLika Plast GmbH | PBT | CompaDur® |
| ICORENE® 5704 | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |
| Hostacom TRC 333N D72714 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Hifax CA 1110 G2 HF C11306 | LyondellBasell Industries | PP Copolymer | Hifax |
| Infino NH-1230 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |