CYCOLAC™ DL100LG resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nhsggb_CYCOLAC-DL100LG-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLAC DL100LG is a low gloss, high heat, high impact ABS/PC blend with low emission |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 10.0 | cm³/10min | |
| 260°C/5.0 kg | 12.0 | cm³/10min | |
| Molding Shrinkage - Flow 1 | 0.50 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 80.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2240 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 47.0 | MPa | ASTM D638 |
| Yield 4 | 51.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/5 |
| Yield | 51.0 | MPa | ISO 527-2/50 |
| Break 5 | 40.0 | MPa | ASTM D638 |
| Break 6 | 38.0 | MPa | ASTM D638 |
| Break | 36.0 | MPa | ISO 527-2/5 |
| Break | 39.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 7 | 4.0 | % | ASTM D638 |
| Yield 8 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5, ISO 527-2/50 |
| Break 9 | 85 | % | ASTM D638 |
| Break 10 | 12 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/5 |
| Break | 12 | % | ISO 527-2/50 |
| Flexural Modulus 11 | 2200 | MPa | ISO 178 |
| Flexural Stress | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 12 | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 380 | J/m | ASTM D256 |
| -30°C 13 | 19 | kJ/m² | ISO 180/1A |
| -30°C 14 | 11 | kJ/m² | ISO 180/1A |
| 23°C 15 | 45 | kJ/m² | ISO 180/1A |
| 23°C 16 | 28 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 17 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 18 | 84.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 118 | °C | ISO 306/A50 |
| -- | 120 | °C | ISO 306/A120 |
| -- | 105 | °C | ISO 306/B50 |
| -- | 107 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 250 to 280 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | Type I, 50 mm/min |
| 9 . | Type I, 5.0 mm/min |
| 10 . | Type I, 50 mm/min |
| 11 . | 2.0 mm/min |
| 12 . | 80*10*3 sp=62mm |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 |
| 15 . | 80*10*3 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 mm |
| 18 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® QC220P | Solvay Specialty Polymers | PPS | Ryton® |
| tefanyl® VE VEEP 115 | Mitsubishi Chemical Performance Polymers, Inc. | PVC+NBR | tefanyl® VE |
| NYLEM® 6 GFR 20 IM | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| Caltex PP MT44 | GS Caltex | PP, Unspecified | Caltex PP |
| Sylvin 5210-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |