Vyncolit® X6952
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nhV7Qr_Vyncolit-X6952.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® X6952 is a glass fiber reinforced phenolic molding compound with superior mechanical properties: highest impact and excellent retention of mechanical properties at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Apparent Density | 0.63 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.14 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.010 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.6 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 18000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 132 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 1.0 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 17000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 255 | MPa | ISO 178 |
| Compressive Stress | 300 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 4.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 224 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.0E-5 | cm/cm/°C | TMA |
| Lateral | 4.1E-5 | cm/cm/°C | TMA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+13 | ohms | IEC 60093 |
| Volume Resistivity | 7.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 38 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa | |
| Screw Speed | 50 | rpm |
| Injection instructions |
|---|
| Injection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time: 5 to 12 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY PA917G6 | Polyram Ram-On Industries | Nylon 66+PP | RAMLLOY |
| TROGAMID® TCR Film 250 µm | Evonik Industries AG | Nylon, Unspecified | TROGAMID® TCR Film |
| NEFTEKHIM PP 5215M (RCXP722) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Niche PCABSN8BK | Niche Polymer, LLC | PC+ABS | Niche |
| Hostacom ERG 393F30 BLACK | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |