Durethan® AKV 30 G HR DUS023 900116
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ngg2Uk_DurethanAKV30GHRDUS023900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 30 % glass fibers, injection molding, improved flowability, hydrolysis stabilized, improved surface finish, GIT/WIT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 290°C, 2.00mm 1 | 0.82 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.040 | -- | % | ISO 294-4 |
| Flow direction : 290°C, 2.00mm 3 | 0.64 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.050 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8500 | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 135 | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.2 | 6.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 8000 | 5600 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | 210 | 130 | MPa | ISO 178/A |
| 23°C | 215 | 150 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.8 | 5.8 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHRW, 14-080, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 8 | 2.00 | -- | J | ISO 6603-2 |
| -- 9 | 2.50 | -- | J | ISO 6603-2 |
| Film Puncture Force | ISO 6603-2 | |||
| -- 10 | 650 | -- | N | ISO 6603-2 |
| -- 11 | 800 | -- | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 70 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 45 | -- | kJ/m² | ISO 180/1U |
| 23°C | 60 | 60 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 75.0 | -- | °C | ISO 75-2/C |
| Melting Temperature 12 | 259 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AZM 23 T6LD | Arkema | Nylon 12 | Rilsan® |
| MIRASON™ C-2494 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| Abstron IMG 1120 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Petrothene® NA443023 (Cast) | LyondellBasell Industries | LDPE+EVA | Petrothene® |
| LNP™ LUBRICOMP™ QCP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |