Auracell® H2
| Category: | CA , Cellulose Acetate |
| Manufacturer: | Rotuba Extruders, Inc. |
| Trademark: | Auracell® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ngLGQ1_Auracell-H2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Auracell® H2 is a Cellulose Acetate (CA) product. It can be processed by injection molding and is available in Europe or North America. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 2.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 33.1 | MPa | |
| Break, 23°C | 43.4 | MPa | |
| Break, 70°C | 22.1 | MPa | |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 1310 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 51.7 | MPa | ASTM D790 |
| Deformation Under Load | ASTM D621 | ||
| 50°C, 6.9 MPa | 1.00 | % | |
| 50°C, 14 MPa | 3.00 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 59 | J/m | |
| 23°C | 190 | J/m |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging - wt. lost, 72 hr (82°C) | 1.2 | wt% | ASTM D706 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flow Beginning Temperature | 160 | °C | ASTM D569 |
| Soluble Matter Loss | 0.20 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -40.0 to -28.9 | °C | |
| Rear Temperature | 216 to 232 | °C | |
| Middle Temperature | 216 to 232 | °C | |
| Front Temperature | 216 to 232 | °C | |
| Nozzle Temperature | 221 to 238 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Injection Pressure | 8.27 to 11.0 | MPa | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Vent Depth | 0.051 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4060 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sylvin 9665-35 Clear Blue 1836 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Bapolene® 1072 | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Axiall PVC 8959 | Axiall Corporation | PVC, Semi-Rigid | Axiall PVC |
| Geon™ Vinyl Flexible 86479 Opaq | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |