POLYblend PC/ABS 65FS GF20
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ngGW2C_POLYblend-PC-ABS-65FS-GF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS-blend Glass fibre-reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.20 to 0.40 | % | |
| Flow | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5700 | MPa | ISO 178 |
| Flexural Stress | 139 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 22 | kJ/m² | |
| 23°C | 22 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 116 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ISO 306/A50 |
| -- | 112 | °C | ISO 306/B50 |
| Ball Pressure Test (115°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PP1MT-3 | Washington Penn Plastic Co. Inc. | PP, Unspecified | WPP PP |
| XYRON™ L542V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| YUCLAIR® DX800 | SK Global Chemical | MDPE | YUCLAIR® |
| COPYLENE® CH085 | Phillips 66 | PP Homopolymer | COPYLENE® |