Chemlon® 66M8
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nf99Cf_Chemlon-66M8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 66M8 is a 40% mineral filled injection moulding grade of nylon 66. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.45 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 1.0 - 1.4 | -- | % | Internal method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5700 | 2500 | MPa | ISO 527-2 |
| Tensile Stress | 100 | 56.0 | MPa | ISO 527-2 |
| Flexural Stress | 160 | 77.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 9.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 40 kJ/m² | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 240 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 165 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm, Teknor Apex test result) | HB | -- | UL 94 | |
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 275 - 295 | °C | |
| Middle Temperature | 275 - 295 | °C | |
| Front Temperature | 275 - 295 | °C | |
| Processing (Melt) Temp | 280 - 295 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | Low | ||
| Screw Speed | Moderate |
| Injection instructions |
|---|
| No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 GA4S01 | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Spartech Polycom M60480 | Spartech Polycom | PVC, Unspecified | Spartech |
| TEREZ PA 6.6 7510 GF 50 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| ALCUDIA® EVA PA-554 | REPSOL | EVA | ALCUDIA® EVA |
| LNP™ LUBRICOMP™ DFL32P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |