CYCOLOY™ LG9000 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nf0DZU_CYCOLOY-LG9000-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ABS blend, low gloss and UV-stable, suitable for automotive interior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | |
| Equilibrium, 23°C | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 54.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 75 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2310 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 84.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 320 | J/m | |
| 23°C | 530 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 33.9 | J | |
| 23°C, Total Energy | 40.7 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 124 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 129 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 107 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 5 |
| CLTE | ASTM E831 | ||
| Flow : -20 to 150°C | 7.2E-5 | cm/cm/°C | |
| Transverse : -20 to 150°C | 7.2E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 30 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 249 to 288 | °C | |
| Middle Temperature | 254 to 293 | °C | |
| Front Temperature | 260 to 302 | °C | |
| Nozzle Temperature | 274 to 302 | °C | |
| Processing (Melt) Temp | 274 to 302 | °C | |
| Mold Temperature | 60.0 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven F-502 | Propilven, S.A. | PP Homopolymer | Propilven |
| Starex NH-0700FX | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Nylene® 5133-02 | Custom Resins Group | Nylon 66 | Nylene® |
| Petlon Prime A2-G30-00-BK | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |
| SABIC® HDPE CC2056 | Saudi Basic Industries Corporation (SABIC) | HDPE Copolymer | SABIC® HDPE |