Durethan® BKV 30 XTS1 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | neN23K_Durethan-BKV-30-XTS1-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, heat-aging stabilized, notably high heat-aging stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.63 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.14 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.25 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.050 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9500 | 5300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 170 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 6.0 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 3.0 | 5.5 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 9400 | 5200 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | -- | 120 | MPa | |
| 23°C 6 | 250 | 140 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | 5.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-100, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 60 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 50 | 70 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.9E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.1E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake PVC 1185B | Westlake Chemical Corporation | PVC, Unspecified | Westlake PVC |
| NORYL™ NH5120 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Arak HDPE EX3 (GM5010T2N) | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| FLEXITEQ™ F90A590 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Pinnacle PP 1120 H | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |