LNP™ LUBRICOMP™ DL002 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ncVVvy_LNPLUBRICOMPDL002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DL002 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DL-4020 Product reorder name: DL002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 53.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 53 | % | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 81.4 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.28 | ASTM D3702 Modified | |
| With Self-Static | 0.17 | ASTM D3702 Modified | |
| Wear Factor - Washer | 97.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 240 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 128 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| HAIPLEN H30 G5 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| EPO-TEK® EE165-3 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Keliren® CM352J | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| Karina IVORY PVC COMPOUND -E 750-35/ 2-IS-SD-TR-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ALTECH® PP-H ECO 4940/500 MR40 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |