VICTREX® PAEK WG™ 102

Category:	PAEK , Polyaryletherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PAEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	nbcz3F_VICTREX-PAEK-WG-102.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, reinforced with wear additives, colour black.
WG102 does not contain polytetrafluoroethylene (PTFE) or other halogenated additives.

Higher temperature tribological applications for high strength and stiffness. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

General Information
Features	Semicrystallization Low friction coefficient Rigidity, high High strength Good liquidity Good chemical resistance Good wear resistance Halogen-free
Appearance	Black
Forms	Particles
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.44	g/cm³	ISO 1183
Spiral Flow ²			Internal method
-- ³	8.50	cm	Internal method
-- ⁴	36.0	cm	Internal method
Molding Shrinkage ⁵			ISO 294-4
Vertical flow direction	0.60	%	ISO 294-4
Flow direction	0.10	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.050	%	ISO 62
Balance, 23°C, 3.20mm, 50% RH	0.50	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 23°C)	86		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	19000	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	190	MPa	ISO 527-2
Fracture, 125°C	130	MPa	ISO 527-2
Fracture, 175°C	85.0	MPa	ISO 527-2
Fracture, 275°C	55.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	2.0	%	ISO 527-2
Flexural Modulus (23°C)	17000	MPa	ISO 178
Flexural Stress			ISO 178
23°C	290	MPa	ISO 178
125°C	220	MPa	ISO 178
175°C	145	MPa	ISO 178
275°C	75.0	MPa	ISO 178
Compressive Stress			ISO 604
23°C	250	MPa	ISO 604
120°C	145	MPa	ISO 604
200°C	75.0	MPa	ISO 604
250°C	55.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	35	kJ/m²	ISO 179/1U
Notched Izod Impact (23°C)	6.0	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	35	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	367	°C	ISO 75-2/Af
Glass Transition Temperature	152	°C	ISO 11357-2
Melting Temperature	373	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : < 143°C	9.0E-6	cm/cm/°C	ISO 11359-2
Flow : > 143°C	1.0E-5	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	3.5E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	9.0E-5	cm/cm/°C	ISO 11359-2
Thermal Conductivity (23°C)	1.3	W/m/K	ISO 22007-4

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ⁶(23°C)	1.0E+7	ohms·cm	IEC 60093

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	600	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	390	°C
Middle Temperature	395 - 400	°C
Front Temperature	405	°C
Nozzle Temperature	410	°C
Mold Temperature	180 - 210	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	Mold temperature: 190°C, melt temperature: 410°C
3 .	1 mm
4 .	3 mm
5 .	410°C nozzle, 190°C tool
6 .	1V

Resin Grade	Manufacturer	Category	Trademark
Telcar® TELC 1000-92 UV-2 BLACK 550	Teknor Apex Company	TPE	Telcar®
Styrolution PS 5310	INEOS Styrolution Group GmbH	PS (HIPS)	Styrolution PS
Sylvin 9450-60 Black	Sylvin Technologies Incorporated	PVC+NBR	Sylvin
OTECH TPR OTR3505-Insoles	OTECH Corporation	TPE	OTECH TPR
Dryflex® V 45A101	ELASTO	TPV	Dryflex®