TABOREN PH 89 T 10
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SILON s.ro |
| Trademark: | TABOREN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nbTGhk_TABOREN-PH-89-T-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TABOREN PH 89 T 10 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 10% talc. It is available in Asia Pacific or Europe. Typical application: Engineering/Industrial Parts. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/1B/50 |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 156 | °C | ISO 306/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 20NSP | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8854 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Formolene® 6501A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| LUBEMID B27 MB NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| Osterlene® HIPS2.63.6 | Osterman & Company | PS (HIPS) | Osterlene® |