Amodel® A-1133 HS Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
AMODEL A- 1133 HS is a 33% glass fiber reinforced thermally stable polyphthalamide (PPA) with high thermal deformation temperature, high bending modulus and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristics of the resin. -Black: A- 1133 HS BK 324 black: A- 1133 HS BK 543 natural color: A- 1133 HS NT

General Information
Filler / Reinforcement	Glass fiber reinforced material, 33% filler by weight
Additive	heat stabilizer
Features	Good dimensional stability Low hygroscopicity Rigidity, high Rigid, good High strength High temperature strength Good creep resistance Good chemical resistance Heat resistance, high
Uses	Power/other tools Industrial components Industrial application Machine/mechanical parts Metal substitution Connector Parts under the hood of a car Automotive Electronics Application in Automobile Field Car interior parts Fuel line Mobile phone Shell
RoHS Compliance	RoHS compliance
UL File Number	E95746
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>PA6T/6I/66-GF33

Physical	Dry	Conditioned	Unit	Test Method
Density	1.48	--	g/cm³	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	0.40	--	%	ASTM D955
Transverse flow	0.80	--	%	ASTM D955
Water Absorption (24 hr)	0.23	--	%	ASTM D570

Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)	125	--		ASTM D785

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	13100	13100	MPa	ASTM D638
23°C	13400	--	MPa	ISO 527-2
100°C	10800	--	MPa	ISO 527-2
150°C	6700	--	MPa	ISO 527-2
175°C	4300	--	MPa	ISO 527-2
Tensile Stress
Fracture, 23°C	233	--	MPa	ISO 527-2
Fracture, 100°C	148	--	MPa	ISO 527-2
Fracture, 150°C	80.0	--	MPa	ISO 527-2
Fracture, 175°C	72.0	--	MPa	ISO 527-2
--	221	193	MPa	ASTM D638
Tensile Elongation
Fracture	2.5	2.1	%	ASTM D638
Fracture, 23°C	2.5	--	%	ISO 527-2
Fracture, 100°C	2.9	--	%	ISO 527-2
Fracture, 150°C	8.7	--	%	ISO 527-2
Fracture, 175°C	8.5	--	%	ISO 527-2
Flexural Modulus
--	11400	11400	MPa	ASTM D790
23°C	11600	--	MPa	ISO 178
100°C	9800	--	MPa	ISO 178
150°C	4000	--	MPa	ISO 178
175°C	3600	--	MPa	ISO 178
Flexural Strength
--	317	254	MPa	ASTM D790
23°C	319	--	MPa	ISO 178
100°C	227	--	MPa	ISO 178
150°C	93.0	--	MPa	ISO 178
175°C	80.0	--	MPa	ISO 178
Compressive Strength	185	--	MPa	ASTM D695
Shear Strength	101	88.9	MPa	ASTM D732
Poisson's Ratio	0.41	--		ASTM E132

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	9.5	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	73	--	kJ/m²	ISO 179/1eU
Notched Izod Impact
--	80	59	J/m	ASTM D256
23°C	8.8	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact
--	770	--	J/m	ASTM D256
23°C	49	--	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, annealed, 3.20mm	297	--	°C	ASTM D648
1.8 MPa, not annealed	280	--	°C	ISO 75-2/A
1.8 MPa, annealed, 3.20mm	285	--	°C	ASTM D648
Continuous Use Temperature				ASTM D3045
-- ¹	164	--	°C	ASTM D3045
-- ²	185	--	°C	ASTM D3045
Melting Temperature	313	--	°C	ASTM D570, ISO 11357-3
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 100°C	2.4E-5	--	cm/cm/°C	ASTM E831
Flow : 100 to 200°C	2.7E-5	--	cm/cm/°C	ASTM E831
Lateral : 0 to 100°C	5.5E-5	--	cm/cm/°C	ASTM E831
Lateral : 100 to 200°C	1.1E-4	--	cm/cm/°C	ASTM E831

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity	1.0E+16	2.0E+15	ohms·cm	ASTM D257
Dielectric Strength (3.20 mm)	21	21	kV/mm	ASTM D149
Dielectric Constant				ASTM D150
60 Hz	4.40	4.70		ASTM D150
1 MHz	4.20	4.30		ASTM D150
Dissipation Factor				ASTM D150
60 Hz	5.0E-3	9.0E-3		ASTM D150
1 MHz	0.017	0.022		ASTM D150
Arc Resistance	140	120	sec	ASTM D495
Comparative Tracking Index (CTI)	550	550	V	UL 746

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating ³(3.20 mm)	HB	--		UL 94

Optical	Dry	Conditioned	Unit	Test Method
Transmittance ⁴				ASTM D1003
1070 nm : 1.60 mm	> 30	--	%	ASTM D1003
940 nm : 1.60 mm	> 30	--	%	ASTM D1003

Additional Information
调节后的 Conditioned to 50% RH in accordance with ISO-1110, Accelerated Method

Injection	Dry	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.045	%
Rear Temperature	304 - 318	°C
Front Temperature	316 - 329	°C
Processing (Melt) Temp	321 - 343	°C
Mold Temperature	135	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Note Message
1 .	20000 hours
2 .	5000 hours
3 .	These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations.
4 .	Light transmittance, natural color only

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	nYRLid_Amodel-A-1133-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Fainplast PVC PK 7075	Fainplast Compounds S.r.l	PVC, Flexible	Fainplast PVC
Plaskon SMT-B-1RC	Cookson Electronics - Semiconductor Products	Epoxy	Plaskon
PENTAMID L GV15 H black	PENTAC Polymer GmbH	Nylon 12	PENTAMID L
WELLAMID Nylon 6000/42 GVS 10/15 HWCP	CP-Polymer-Technik GmbH & Co. KG	Nylon 6	WELLAMID Nylon
POCAN® DP 2004 000000	LANXESS GmbH	PBT	POCAN®