Petrothene® NA983085
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nXQW4L_Petrothene-NA983085.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA983085 is a low density homopolymer resin selected by customers for use in shrink packaging, bundling, pallet wrap and heavy-duty liner applications. Excellent bubble stability, melt strength, impact and shrinkage are key attributes of NA983985. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D1505 | ||
| -- 1 | 0.920 | g/cm³ | |
| -- | 0.922 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm, Blown Film | 207 | MPa | |
| 1% Secant, TD : 32 µm, Blown Film | 241 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, Blown Film | 20.7 | MPa | |
| TD : Yield, 32 µm, Blown Film | 19.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 310 | % | |
| TD : Break, 32 µm, Blown Film | 430 | % | |
| Dart Drop Impact (32 µm, Blown Film) | 180 | g | ASTM D1709 |
| Note Message | |
|---|---|
| 1 . | Base Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EVATHENE® UE632 | USI Corporation | EVA | EVATHENE® |
| Di-Pak™ R-4545/40 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Duratron® T4301 (EXTRUSION) | Quadrant Engineering Plastic Products | PAI | Duratron® |
| Grilon® R 50 H NZ | EMS-GRIVORY | Nylon 6 | Grilon® |
| Infino AR-5300H | SAMSUNG SDI CO., LTD. | PBT+ASA | Infino |