RIALFILL CE 02 SN 40 C3
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nX6iVH_RIALFILL-CE-02-SN-40-C3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer impact modified 40% filled with calcium carbonate thermal stabilization of process. Low flowability suitable for injection molding and extrusion. Excellent impact strength and tenacity properties up to low temperature (still -40°C), good dimensional stability. Available in the versions natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.95 | % | |
| Flow | 0.95 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 40 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 18.0 | MPa | |
| Break, 23°C | 16.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | > 350 | % | |
| Flexural Modulus 2(23°C) | 2000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 34.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 4.5 | kJ/m² | |
| -20°C | 6.0 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/A50 |
| -- | 68.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH RZ300G2 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Veradel® 3600P | Solvay Specialty Polymers | PESU | Veradel® |
| DOW™ LDPE 515E | The Dow Chemical Company | LDPE | DOW™ LDPE |
| biofila® silk | twoBEars GbR | Biodeg Polymers | biofila® |
| Jiangsu Sinarise ZM928 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |